H13钢表面熔覆工艺的研究
Study on Surface Cladding Process for H13 Steel
王希靖, 吴红林, 刘 骁, 朱正泽
点击：5179次 下载：0次
作者单位：兰州理工大学 甘肃省有色金属新材料甘肃重点实验室, 甘肃 兰州 730050
中文关键字：激光熔覆； 工艺参数； 显微组织； 显微硬度； 耐磨性
英文关键字：laser cladding; craft parameter; microstructure; micro hardness; abrasive resistance
中文摘要：采用10 kW的CO2激光器在H13钢基体上熔覆一层镍基粉末，研究了激光加工工艺参数(激光功率、扫描速度等)对熔覆层组织、硬度和摩擦磨损性能的影响。结果表明，该镍基涂层和基体形成了良好的冶金结合，硬度和耐磨性能有了明显提高。最佳工艺参数为：激光功率2 kW，扫描速度200～300 mm/min。
英文摘要：Ni-based alloy coating on the surface of H13 steel substrate was obtained using 10 kW continuous wave CO2 laser. The influences of laser technological parameters (laser power, scanning velocity) on the microstructure, microhardness and wear and friction attrition performance were studied. The results show that the good metallurgy bending between the nickel based coating and the substrate forms; the hardness and wear-resisting performance obviously increase. The superior technological parameter is that the power of laser cladding is 2 kW and the scanning speed is 200～300 mm/min．