Ni-P-MoS2复合镀层的制备和耐磨性能研究
Preparation of Ni-P-MoS2 Composite Coating and Study on Its Wear Resistance
朱乃龙, 杨顺贞, 纪秀林
点击:3595次 下载:0次
作者单位:(河海大学 机电工程学院, 江苏 常州 213022)
中文关键字:复合镀层; 电沉积; 耐磨性能
英文关键字:composite electrodeposition; MoS2; Ni-P; wear resistance
中文摘要:采用电沉积法制备Ni-P-MoS2复合镀层,研究了镀液中纳米MoS2含量与沉积速度的关系,分析了MoS2添加量对镀层显微硬度以及耐磨性能的影响。结果表明,当纳米MoS2在镀液中的加入量为4 g/L时,镀层的耐磨性能得到改善,磨损质量损失为普通Ni-P镀层的55%,经400 ℃ × 1 h热处理后复合镀层表现出更好的耐磨性能。
英文摘要:i-P-MoS2 composite coating was prepared by electro-deposition. The relationship between addition amount of nano-particles in electroplating solution and depositing rate of the coating was studied. The influences of addition amount of nano-particles on micro-hardness and wear resistance were analyzed. The results show that the wear resistance improves when the adding amount of MoS2 is 4 g/L. Wear mass loss of Ni-P- MoS2 composite coating is 55% of normal Ni-P coating. After heat treatment at 400 ℃ for 1 h, Ni-P- MoS2 composite coating shows better wear resistance.