5Cr冷轧辊多次调质处理研究
Study on Multiple Quenching and Tempering of 5%Cr Cold Roll
李春光1, 孙大乐2, 周 利1, 刘光明1
点击:3524次 下载:0次
作者单位:1.首钢技术研究院, 北京 100043; 2. 宝山钢铁股份有限公司 研究院, 上海 201900)
中文关键字:冷轧辊; 调质处理; 性能; 组织
英文关键字:cold roll; quenching and tempering; mechanical properties; microstructure
中文摘要:为探索报废冷轧辊改制成小辊径冷轧辊的可行性,研究了多次调质处理对5Cr冷轧辊材料性能和组织的影响。结果表明:报废冷轧辊料经过一次调质或二次调质的组织和性能可达到冷轧辊的使用要求,但调质处理不能超过二次。
英文摘要:The feasibility of scrapping large diameter roll restructuring small diameter roll was explored. The influences of multiple quenching and tempering on microstructure and mechanical properties of 5Cr cold roll were studied. The results show that operating requirements can be satisfied with microstructure and mechanical properties after once or twice multiple heat treatment and quenching and tempering number of times is not more than twice.